Effect of different additives on the ball milling process during operation of the ball mill, various process parameters have a milling process produces a large or small impact, such as ball diameter, additive nature, etc., wherein the additive's role is to regulate the milling tank The physical properties of materials and operational status, the following analysis will focus on the effects of different additives on the ball milling process. Conduct analysis for the three trials, choose different additives: add water without ethanol 6mL, plus stearate 5g, no additives, to analyze the impact of the milling process. Test results at right: Since liquid ethanol can carry and disperse the powder, and the powder can reduce the surface energy and play a role in the absorption of heat, during the milling process, the appropriate amount of ethanol was added to make a paste powder distribution on the ball and the inner wall of the tank, powder thinning rate is higher than the other two groups. Milling is a high-energy ball milling method, ball mill price, ball milling process, the consumption of alcohol quickly, experiment 4h milling ethanol almost spent, continue milling agglomeration is generated, a dry ball mill, caking even more than the last group the degree of blocking dry grinding. According to the test results, in the first set of tests, to ensure good wet-milling state, controlling the amount of ethanol added is the key addition of the slurry will be too thin too, powder adhesion on the ball will be weakened; too small an amount, the slurry is too thick, make the ball movement difficult, mill manufacturers, and too thick slurry easy to agglomerate. In the second group, stearic acid is a solid surfactant, which can effectively prevent the oxidation of powder, its friction reduction and dispersion powder is very clear, and the refinement of the lowest rate of the test material . To sum up: the effect of wet grinding mill is far better than the situation without dry grinding dry grinding and processing of solid acid additives, not only high efficiency refining powder, the powder can effectively prevent caking, oxidation and so on, but it must be added to control the amount of wet milling additives. Ball routine examination should pay attention to local mill itself inspection include the following: 1, be careful to check for loose screws ministries, especially the liner screw loose, pull off, resulting in leakage of plasma; this is best when each shift conduct, all connecting bolts fastening Check mill group, if there is loose must stop tightening. 2. Check the return sand spoon head wear; regularly check lining wear, wear should be replaced to a certain extent 3, attention mill nesting run rough or spit balls. Second ball mill supply system check: 1, always check the oil pressure is normal, Liaoyang ball, should be maintained at 1.5 ~ 2.0 kg / cm2.2, check the oil and the oil temperature, oil temperature should not exceed 30 ℃. 3. Check the main journal oil flow distribution is uniform. 4, oil viscosity and cleanliness. Mill Motor inspection: the main check motor temperature, which temperature does not exceed the permissible value last mill grading equipment inspection: 1. Check blade spiral classifier is off, turn smoothly. 2, cyclone for the ore pressure is stable, if there is ground leak or clogging. Liaoyang ball | North Mine Zhongcheng | Slag Ball from Shenyang North Mine Zhongcheng machinery Limited. Liaoyang ball | North Mine Zhongcheng | slag mill Shenyang North Mine Zhongcheng equipment Limited (sybkzc.com) (www.sybkzcjq.com) this year introduced a new upgrade, the above picture is for reference only, please call this page or Tel picture on to obtain the latest information, contact: Yang Zhongbin.